■ Overview
High strength cold forming finished rectangular hollow sections S355J2H in european standard EN 10219-1 with minimum yield strength at 355Mpa and tensile strength at 510Mpa when offering.Xinsteel keeps all kinds of stock hot formed and cold formed rectangular tubes,rectangular hollow sections and rectangular pipes.
■ Full Data
Technical Requirements & Additional Services:
♦ Low temperature impacting test according to EN10045-1
♦ Wall thickness tolerance according to EN10210-2
♦ Ultrasonic test under EN 10160,ASTM A435,A577,A578
♦ Issued Orginal Mill test certificate under EN 10204 FORMAT 3.1/3.2
♦ Surface Protection:Black,Varnish,Hot Dip Galvanized,Pre-Galvanized,Coating with shop prime.
♦ Low temperature impacting test according to EN10045-1
♦ Wall thickness tolerance according to EN10210-2
♦ Ultrasonic test under EN 10160,ASTM A435,A577,A578
♦ Issued Orginal Mill test certificate under EN 10204 FORMAT 3.1/3.2
♦ Surface Protection:Black,Varnish,Hot Dip Galvanized,Pre-Galvanized,Coating with shop prime.
■ Techicals
►Mechnical property for S355J2H Rectangular Hollow Sections:
|
Thickness (mm) |
||||||
|
|
≤ 16 |
> 16 ≤ 40 |
> 40 ≤ 63 |
> 63 ≤ 80 |
> 80 ≤ 100 |
> 100 ≤ 120 |
|
Yield strength (≥Mpa) |
355 |
345 |
335 |
325 |
315 |
295 |
|
|
< 3 |
≥ 3 ≤ 100 |
> 100 ≤ 120 |
|||
|
Tensile strength (Mpa) |
510-680 |
470-630 |
450-600 |
|||
►Chemical composition for S355J2H Rectangular Hollow Sections (Ladle Analysis Max%)
|
Main chemical elements composition of S355J2H |
||||||
|
Thickness(mm) |
C |
Si |
Mn |
P |
S |
N |
|
T≤40 |
0.22 |
0.55 |
1.60 |
0.030 |
0.030 |
|
|
40<T≤120 |
0.22 |
|||||