■ Overview
Xinsteel keeps all kinds of stock hot formed and cold formed galvanized square tubes Q295A,galvanized square hollow sections Q295A and sml square pipes Q295A.The manufacturing processes of hot finished and cold formed hollow sections are very different.Hot finished hollow sections are formed at normalising temperature (approx 900°C).Cold formed hollow sections are formed at ambient temperature.
■ Full Data
Technical Requirements & Additional Services:
♦ Galvanized coating according to GB/T 13912
♦ Dimension tolerance according to GB/T6728
♦ Ultrasonic test under EN 10160,ASTM A435,A577,A578
♦ Issued Orginal Mill test certificate under EN 10204 FORMAT 3.1/3.2
♦ Surface Protection:Black,Varnish,Hot Dip Galvanized,Coating with shop prime.
♦ Galvanized coating according to GB/T 13912
♦ Dimension tolerance according to GB/T6728
♦ Ultrasonic test under EN 10160,ASTM A435,A577,A578
♦ Issued Orginal Mill test certificate under EN 10204 FORMAT 3.1/3.2
♦ Surface Protection:Black,Varnish,Hot Dip Galvanized,Coating with shop prime.
■ Techicals
►Mechnical property for Q295A structural steel hollow section:
|
Thickness (mm) |
|
|
Q295A |
|
|
Yield strength (≥Mpa) |
295 |
|
Tensile strength (Mpa) |
390-570 |
►Chemical composition for Q295A structural steel hollow section (Heat Analysis Max%)
|
Main chemical elements composition of Q295A |
|||||||
|
C |
Si |
Mn |
P |
S |
V |
Nb |
Ti |
|
0.16 |
0.55 |
0.80-1.50 |
0.045 |
0.045 |
0.02-0.15 |
0.015-0.060 |
0.02-0.20 |