■ Overview
High strength square hollow sections S460MH in european standard EN 10219-1 with minimum yield strength at 460Mpa and low temperature impacting test at minus 20 Deg.C.Xinsteel stockholder thousands tons different sizes of hot rolled hot formed finished square hollow section S460MH with seamless type and welded type.
■ Full Data
Technical Requirements & Additional Services:
♦ Low temperature impacting test according to EN10045-1
♦ Wall thickness tolerance according to EN10210-2
♦ Ultrasonic test under EN 10160,ASTM A435,A577,A578
♦ Issued Orginal Mill test certificate under EN 10204 FORMAT 3.1/3.2
♦ Surface Protection:Black,Varnish,Hot Dip Galvanized,Pre-Galvanized,Coating with shop prime.
♦ Low temperature impacting test according to EN10045-1
♦ Wall thickness tolerance according to EN10210-2
♦ Ultrasonic test under EN 10160,ASTM A435,A577,A578
♦ Issued Orginal Mill test certificate under EN 10204 FORMAT 3.1/3.2
♦ Surface Protection:Black,Varnish,Hot Dip Galvanized,Pre-Galvanized,Coating with shop prime.
■ Techicals
►Mechnical property for S460MH Hollow Sections:
|
Thickness (mm) |
|||||
|
|
≤ 16 |
> 16 ≤ 40 |
> 40 ≤ 65 |
Impact temperature |
Min.Energy |
|
Yield strength (≥Mpa) |
460 |
440 |
430 |
℃ |
J |
|
Tensile strength (Mpa) |
550-720 |
-20 |
40 |
||
►Chemical composition forS460MH Hollow Sections (Heat Analysis Max%)
|
Main chemical elements composition of S460MH |
||||||
|
C |
Si |
Mn |
P |
S |
Nb |
V |
|
0.20 |
0.60 |
1.00-1.70 |
0.035 |
0.030 |
0.050 |
0.20 |
|
Alt min. |
Ti |
Cr |
Ni |
Mo |
Cu |
N |
|
0.02 |
0.03 |
0.03 |
0.80 |
0.10 |
0.70 |
0.025 |