■ Overview
Square hollow sections S275MLH in EN 10219 is inherently strong and efficient.These sections S275MLH tubes shall be done TMCP and low temperature impacting test.Xinsteel keeps ready shipment stock for these welded square hollow sections S275MLH,welded square tubes S275NL1 and seamless square pipes S275MLH.
■ Full Data
Technical Requirements & Additional Services:
♦ Low temperature impacting test according to EN10045-1
♦ Wall thickness tolerance according to EN10210-2
♦ Ultrasonic test under EN 10160,ASTM A435,A577,A578
♦ Issued Orginal Mill test certificate under EN 10204 FORMAT 3.1/3.2
♦ Surface Protection:Black,Varnish,Hot Dip Galvanized,Pre-Galvanized,Coating with shop prime.
♦ Low temperature impacting test according to EN10045-1
♦ Wall thickness tolerance according to EN10210-2
♦ Ultrasonic test under EN 10160,ASTM A435,A577,A578
♦ Issued Orginal Mill test certificate under EN 10204 FORMAT 3.1/3.2
♦ Surface Protection:Black,Varnish,Hot Dip Galvanized,Pre-Galvanized,Coating with shop prime.
■ Techicals
►Mechnical property for S275MLH Hollow Sections:
|
Thickness (mm) |
||||
|
|
≤ 16 |
> 16 ≤ 40 |
Impact temperature |
Min.Energy |
|
Yield strength (≥Mpa) |
275 |
265 |
℃ |
J |
|
Tensile strength (Mpa) |
360-510 |
-50 |
27 |
|
►Chemical composition forS275MLH Hollow Sections (Heat Analysis Max%)
|
Main chemical elements composition of S275MLH |
||||||
|
C |
Si |
Mn |
P |
S |
Nb |
V |
|
0.13 |
0.50 |
1.50 |
0.030 |
0.025 |
0.050 |
0.08 |
|
Alt min. |
Ti |
Ni |
Mo |
N |
|
|
|
0.02 |
0.05 |
0.30 |
0.20 |
0.020 |
|
|