■ Overview
High strength rectangular hollow sections S355J2H in european standard EN 10210-1 with minimum yield strength at 355Mpa and tensile strength at 510Mpa when offering.Xinsteel stockholder thousands tons different sizes of hot rolled hot formed finished square hollow section S355J2H with seamless type and welded type.
■ Full Data
Technical Requirements & Additional Services:
♦ Low temperature impacting test according to EN10045-1
♦ Wall thickness tolerance according to EN10210-2
♦ Ultrasonic test under EN 10160,ASTM A435,A577,A578
♦ Issued Orginal Mill test certificate under EN 10204 FORMAT 3.1/3.2
♦ Surface Protection:Black,Varnish,Hot Dip Galvanized,Pre-Galvanized,Coating with shop prime.
♦ Low temperature impacting test according to EN10045-1
♦ Wall thickness tolerance according to EN10210-2
♦ Ultrasonic test under EN 10160,ASTM A435,A577,A578
♦ Issued Orginal Mill test certificate under EN 10204 FORMAT 3.1/3.2
♦ Surface Protection:Black,Varnish,Hot Dip Galvanized,Pre-Galvanized,Coating with shop prime.
■ Techicals
►Mechnical property for S355J2H Rectangular Hollow Sections:
|
Thickness (mm) |
||||||
|
|
≤ 16 |
> 16 ≤ 40 |
> 40 ≤ 63 |
> 63 ≤ 80 |
> 80 ≤ 100 |
> 100 ≤ 120 |
|
Yield strength (≥Mpa) |
355 |
345 |
335 |
325 |
315 |
295 |
|
|
< 3 |
≥ 3 ≤ 100 |
> 100 ≤ 120 |
|||
|
Tensile strength (Mpa) |
510-680 |
470-630 |
450-600 |
|||
►Chemical composition for S355J2H Rectangular Hollow Sections (Ladle Analysis Max%)
|
Main chemical elements composition of S355J2H |
||||||
|
Thickness(mm) |
C |
Si |
Mn |
P |
S |
N |
|
T≤40 |
0.22 |
0.55 |
1.60 |
0.030 |
0.030 |
|
|
40<T≤120 |
0.22 |
|||||