Our engineers suggest that for thickness belows and equal to 100mm,Normalized and Tempered heat treatment for 13CrMo4-5,13CrMo4-5 steel plate,13CrMo4-5 steel sheet,for thickness within 100-150mm,Normalized and Tempered or Quenched and Tempered are both ok,for thickness above 150mm,Quenched and Tempered are necessary.If resistance to pressurized hydrogen is of importance, a minimum content of 0,80% Cr may be agreed upon at the time of enquiry and order.
♦ High tension test
♦ Low temperature impacting test
♦ Simulated post-welded heat treatment (PWHT)
♦ Ultrasonic test under EN 10160,ASTM A435,A577,A578
♦ Issued Orginal Mill test certificate under EN 10204 FORMAT 3.1/3.2
♦ Shot blasting and Painting,Cutting and welding as per end user’s demands
►Mechnical property for 13CrMo4-5 steel plate:
Thickness(mm) | Yield strength (≥Mpa) | Tensile strength (Mpa) | Elongation in ≥,% |
T≤16 | 300 | 450-600 | 19 |
16<T≤60 | 290 | ||
60<T≤100 | 270 | 440-590 | |
100<T≤150 | 255 | 430-580 | |
150<T | 245 | 420-570 |
►Chemical composition for 13CrMo4-5 steel plate (Heat Analysis Max%)
Main chemical elements composition of 13CrMo4-5 steel plate | ||||||||||
C | Si | Mn | P | S | N | Cr | Cu | Mo | Ni | Nb |
0.08-0.18 | 0.35 | 0.40-1.00 | 0.025 | 0.010 | 0.012 | 0.70-1.15 | 030 | 0.40-0.60 | 0.40-0.80 | 0.015-0.045 |