HOT ROLLED STAINLESS PLATE A240 TP 321H

HOT ROLLED STAINLESS PLATE A240 TP 321H shall be produced complying to specification A240 / A240M OR SA240 / SA240M,Brinell hardness shall be Maximum 217 HBW,and Rockwell Hardness Maximum 95 HRBW.Hardness test is permitted to perform on the grip ends of the tension specimens before they are subjected to the tension test.Cold Bend is not required for stainless steel plate A240 321H.

Technical Requirements & Additional Services for HOT ROLLED STAINLESS PLATE A240 TP 321H:
♦  Ultrasonic examination comply to A578/A578M A577/A577M A435/A435M
♦  A240 321H is enhanced creep resistance and for higher strength at higher temperature
♦  Issued Orginal Mill test certificate under EN 10204 FORMAT 3.1/3.2 
♦  PMI test report,Cutting and welding as per end user’s demands 
♦  Packing with water-resistance paper and Non-fumigation wooden crates
♦  Paper Interleave,Polyethylene Film coating （PE COAT）for cold rolled stainless steels

►Mechnical property for HOT ROLLED STAINLESS PLATE A240 TP 321H

Stainless steel plate A240 321H
Yield strength (≥Mpa)	Tensile strength (≥Mpa)	Elogation in 50mm min. %	Hardness, Max
			Brinell HBW	Rockwell HRBW
205	515	40	217	95

►Chemical composition for HOT ROLLED STAINLESS PLATE A240 TP 321H (Heat Analysis Max%)

Main chemical elements composition of stainless steel plate A240 321H
C	Mn	P	S	Si	Cr
0.04-0.10	2.00	0.045	0.030	0.75	17.0-19.0
Ni	Mo	N	Cb	Al	Ti
9.0-12.0	-	-	-	-	4*(C+N)-0.70