■ Overview
A204 Grade C,A204GrC steel plate,A204GrC steel sheet owned yield strength above 295 Mpa,tensile strength within 515-655 Mpa.The Elongation percent of A204GrC steel sheet in 200mm shall be equal or above 16,and the elongation percent in 50mm shall be equal or above 20.A204 Grade C steel plate for pressure vessel is Molybdenum alloy steel plates.The chemical element Mo contains shall be within 0.45-0.60 for heat analysis when rolling.XINSTEEL would like to offer superior quality boiler steel plate SA204 Grade C with ABS,TUV,CE,DNV approved.
■ Full Data
Technical Requirements & Additional Services for A204GrC steel plate:
♦ High tension test
♦ Low temperature impacting test
♦ Normalised for thick plates over 40mm
♦ Simulated post-welded heat treatment (PWHT)
♦ Rolling under standard NACE MR-0175 (HIC+SSCC)
♦ Issued Orginal Mill test certificate under EN 10204 FORMAT 3.1/3.2
♦ Shot blasting and Painting,Cutting and welding as per end user’s demands
♦ High tension test
♦ Low temperature impacting test
♦ Normalised for thick plates over 40mm
♦ Simulated post-welded heat treatment (PWHT)
♦ Rolling under standard NACE MR-0175 (HIC+SSCC)
♦ Issued Orginal Mill test certificate under EN 10204 FORMAT 3.1/3.2
♦ Shot blasting and Painting,Cutting and welding as per end user’s demands
■ Techicals
► Mechnical property for A204GrC steel plate:
Yield strength (≥Mpa) | Tensile strength (Mpa) | Elongation in ≥,% | |
295 | 515-655 | 200mm | 50mm |
16 | 20 |
►Chemical composition for A204 Grade C steel plate (Heat Analysis Max%)
Main chemical elements composition of A204 Grade C steel plate | ||||||
Thickness(mm) | C | Si | Mn | P | S | Mo |
T≤25 | 0.23 | 0.15-0.40 | 0.90 | 0.035 | 0.035 | 0.45-0.60 |
25<T≤50 | 0.26 | |||||
50<T≤100 | 0.28 | |||||
T>100 | 0.28 |