■ Overview
Hot finished and cold drawing A210 Grade C seamless tube,A210 grade C steel pipe,A210 C steel tube supplying from China stock warehouses.Comparasion with A210 Grade A-1 seamless tube,A210 Grade C seamless tube contains a higher carbon percentage in chemical composition and higher yield strength and tensile strength values.
■ Full Data
Technical Requirements & Additional Services for A210 Grade C Seamless Steel Tube:
♦ A210 Grade C steel materials shall be killed.
♦ Ultrasonic test under GB/T 5777,EN 10160,ASTM A435,A577,A578
♦ General requirements for A210-C steel tubes according to A450/A450M
♦ Issued Orginal Mill test certificate under EN 10204 FORMAT 3.1/3.2
♦ Surface Protection:Black,Pickling,Varnish,Hot Dip Galvanized,Coating with shop prime.
♦ Cold finished A210 C steel tubes shall be done subcritical anneal or full anneal or Normalizing heat treatment.
♦ A210 Grade C steel materials shall be killed.
♦ Ultrasonic test under GB/T 5777,EN 10160,ASTM A435,A577,A578
♦ General requirements for A210-C steel tubes according to A450/A450M
♦ Issued Orginal Mill test certificate under EN 10204 FORMAT 3.1/3.2
♦ Surface Protection:Black,Pickling,Varnish,Hot Dip Galvanized,Coating with shop prime.
♦ Cold finished A210 C steel tubes shall be done subcritical anneal or full anneal or Normalizing heat treatment.
■ Techicals
►Mechnical property for A210 Grade C Seamless Steel Tube:
Thickness (mm) |
|
A210-C |
|
Yield strength (≥Mpa) |
275 |
Tensile strength (≥Mpa) |
485 |
►Chemical composition for A210 Grade C Seamless Steel Tube (Heat Analysis Max%)
Main chemical elements composition of A210-C |
||||
C |
Si |
Mn |
P |
S |
0.35 |
0.10 |
0.29-1.06 |
0.035 |
0.035 |